What is the hardness of stainless steel 316?

What is the hardness of stainless steel 316?

On the Brinell hardness scale 316 stainless steel plate has a hardness of 217 and a Rockwell B hardness of 95. There are a few differences in mechanical properties between 316 and 316L stainless steel plate. One of these difference lies in the tensile strength.

How hard is stainless steel Rockwell?

The Rockwell rating is a scale that is used to measure the hardness of a material. An example is stainless steel AUS-8, which usually 57-59 Rc. The Rockwell hardness test is the industry standard for knives.

What is the Rockwell C hardness of 304 stainless steel?

15 15
AISI Type 304L Stainless Steel

Physical Properties Metric English
Hardness, Rockwell C 15 15
Hardness, Vickers 159 159
Tensile Strength, Ultimate 564 MPa 81800 psi
Tensile Strength, Yield 210 MPa 30500 psi

What is the difference between SS 316 and 316L?

316L stainless steel is almost identical to 316. The only difference is the carbon content. 316L’s lower carbon content imparts even better corrosion resistance than 316. 316L does not require post-weld annealing.

What does a high Vickers hardness number mean?

It is defined as the resistance to indentation, and it is determined by measuring the permanent depth of the indentation. More simply put, when using a fixed force (load) and a given indenter, the smaller the indentation, the harder the material.

What does 60 HRC mean?

A lower Rockwell number means that the steel is softer, relatively speaking, while a higher number indicates a harder steel. Sometimes you’ll see Rockwell hardness expressed as a single value, like “59 RC,” and other times as a range, like “58-60 HRC.”

What is the shear modulus of 316L steel?

Stainless Steel 316 has superior corrosion resistance properties as well as elevated Poisson ratio 0.265 to 0.275 Shear modulus 74 to 82 Gpa or 10.7 to 11.8 x 10(6) psi Welding: Steel 316L can be easily welded through common methods. The post weld heat

What is the difference between AISI 316 and SS 316?

Due to the addition of Molybdenum (Mo), SS 316 has a great improvement in corrosion resistance and certain properties. 316L stainless steel (UNS S31603) is the low carbon version of AISI 316.

What is the specific heat capacity of 316 stainless steel?

Density of stainless steel 316 (g/cm3) 8.03: Melting point of stainless steel 316: 1370-1398 ℃ Specific heat capacity, J/(Kg·K) 502 at 20 ℃ Electrical resistivity, μΩ·m: 0.74 (20 ℃) Magnetic permeability: 1.02 (Approximate) Modulus of elasticity (Elastic modulus), GPa: 193 (28×10 6 psi) Thermal diffusivity, mm2/s: 4.05 (20-100 ℃)

What is the typical forging temperature of 316 stainless steel?

AISI 316 stainless steel typical forging temperature is 925-1260 °C (1700-2300 ℉). Type 316 SS cannot be hardened by heat treatment, but can be hardened by cold working.